Stainless Steel Pipe
Stainless Steel Pipe
316L Stainless Steel Pipe
316L stainless steel has a lower proportion of carbon in its composition, the amount of carbon cannot go over 0.03%. This lowers the chance of carbon precipitation, making it an ideal option for welding to ensure maximum corrosion resistance.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
316L Stainless Steel Pipe Description
316L stainless steel is an austenitic stainless steel metal alloy that contains nickel and molybdenum, making it corrosion resistant. 316L is a 316 low carbon grade. This grade is not affected by sensitization (grain boundary carbide precipitation). It is often used for large-gauge welded parts (approximately over 6mm). 316L stainless steel has higher creep, fracture stress and tensile strength than chromium nickel austenitic stainless steel at high temperature.
Product Parameters
Product Name 316L Stainless Steel Pipe Type Steel Pipe Outer diameter Round Tube 4mm-200mm Square Tube 10*10mm-100*100mm Rectangular Tube 10*20mm-50*100mm Wall Thickness 0.6mm-6.0mm Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. Scope of Application Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P Mo ≤ 0.03 ≤1.0 ≤ 2.0 16.0～18.0 10.0～14.0 ≤ 0.03 ≤ 0.045 2.0～3.0
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥480 ≥177 ≥ 40 ≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(ΜΩ. cm) 7.99 193 16.0 16.2 74