Stainless Steel Pipe
Stainless Steel Pipe
304L Stainless Steel Pipe
304L stainless steel has a very similar chemical composition to 304 stainless steel with one key difference. The maximum carbon content is set at 0.08% for 304, whereas grade 304L stainless steel has a maximum carbon content of 0.03%. It is more often adopted in the production of equipment and parts that require better corrosion resistance.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
304L Stainless Steel Pipe Description
304L is one of the austenitic stainless steels with a chromium content of at least 18%, a nickel content of at least 8%, and a maximum carbon content of 0.03. 304L stainless steel is an ideal choice for various household and commercial applications, with excellent corrosion resistance, ease of manufacturing and excellent formability. Austenitic stainless steels are also considered to be the easiest to weld among high alloy steels and can be welded by all fusion and resistance welding processes.
Product Parameters
Product Name 304L Stainless Steel Pipe Type Steel Pipe Outer diameter Round Tube 4mm-200mm Square Tube 10*10mm-100*100mm Rectangular Tube 10*20mm-50*100mm Wall Thickness 0.6mm-6.0mm Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. Scope of Application Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.03 ≤1.0 ≤ 2.0 18.0～20.0 8.0～12.0 ≤ 0.03 ≤ 0.035
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥ 520 ≥ 205 ≥ 40 ≤ 187HB ;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(ΜΩ. cm) 8.03 193 16.9 16.2 72