Stainless Steel Coil
Stainless Steel Coil
301 Stainless Steel Coil
301 stainless steel is an austenitic stainless steel with 17 percent chromium and 7 percent nickel, ensuring good strength and ductility when cold worked. Besides, it also has excellent corrosion resistance properties.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
301 Stainless Steel Coil Description
301 grade stainless steel is a common austenitic stainless steel with good corrosion resistance and high carbon content, and can be cold worked to various temperatures. Among stainless steels, 301 is the most easily strengthened steel by cold deformation. Cold deformation processing can improve the strength and hardness of steel, and retain sufficient plasticity and toughness. In addition, this steel has good rust resistance under atmospheric conditions, but its corrosion resistance in reducing media is poor, and its corrosion resistance in chemical media such as acid, alkali and salt is poor. Therefore, it is not recommended for corrosive environments.
Product Parameters
Product Name 301 Stainless Steel Coil Type Steel Coil Thickness 2.5mm-10.0mm Length 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. Width 610mm-2000mm Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. Scope of Application Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.15 ≤1.0 ≤ 2.0 16.0～18.0 6.0～8.0 ≤ 0.03 ≤ 0.045
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥ 520 ≥ 205 ≥ 40 ≤ 187HB ;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(μohm.in) 7.88 193 16.9 16.2 27.4
Surface Selection