Stainless Steel Coil
Stainless Steel Coil
316L Stainless Steel Coil
316L stainless steel features a lower proportion of carbon in its composition. The amount of carbon cannot be higher 0.03%. This lowers the risk of carbon precipitation, making it a better option for welding to achieve maximum corrosion resistance.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
316L Stainless Steel Coil Description
316L stainless steel is an austenitic stainless steel metal alloy that contains nickel and molybdenum, making it corrosion resistant. 316L is a 316 low carbon grade. This grade is not affected by sensitization (grain boundary carbide precipitation). It is often used for large-gauge welded parts (approximately over 6mm). 316L stainless steel has higher creep, fracture stress and tensile strength than chromium nickel austenitic stainless steel at high temperature.
Product Parameters
Product Name 316L Stainless Steel Coil Type Steel Coil Thickness 2.5mm-10.0mm Length 2000mm, 2440mm, 3000mm, 5800mm, 6000mm, etc. Width 610mm-2000mm Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. Scope of Application Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P Mo ≤ 0.03 ≤1.0 ≤ 2.0 16.0～18.0 10.0～14.0 ≤ 0.03 ≤ 0.045 2.0～3.0
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥480 ≥177 ≥ 40 ≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(ΜΩ. cm) 7.99 193 16.0 16.2 74
Surface Selection