Carbon Steel Plate
Carbon Steel Plate
1018 Cold Rolled Steel Plate
There are many different categories of steel, and carbon steels are one such category that contains 0.12 to 2% carbon in them. The steel gains hardness and strength with heat treatment when the carbon percentage content increases; however its ductility is reduced.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
1018 Cold Rolled Steel Plate
There are many different categories of steel, and carbon steels are one such category that contains 0.12 to 2% carbon in them. The steel gains hardness and strength with heat treatment when the carbon percentage content increases; however its ductility is reduced.
AISI 1018 carbon steel is a free machining grade that is the most commonly available grade around the world. Although its mechanical properties are not very unique, it still can be easily formed, machined, welded and fabricated.
The following sections will discuss in detail about AISI 1018 carbon steel.
Product Parameters
Product Name | 1018 Cold Rolled Steel Plate |
Production Process | Hot Rolling, Cold Rolling |
Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
Width | 100mm-3000mm |
Length | 1m-12m, or Customized Size |
Thickness | 0.1mm-400mm |
Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Manganese, Mn | 0.60-0.90 |
| Carbon, C | 0.15-0.20 |
| Sulfur, S | 0.05 (max) |
| Phosphorous, P | 0.04 (max) |
| Iron, Fe | Balance |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 440 MPa | 63800 psi |
| Yield strength | 370 MPa | 53700 psi |
| Modulus of elasticity | 205 GPa | 29700 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poisson’s ratio | 0.29 | 0.29 |
| Elongation at break (in 50 mm) | 15 % | 15 % |
| Hardness, Brinell | 126 | 126 |
| Hardness, Knoop (converted from Brinell hardness) | 145 | 145 |
| Hardness, Rockwell B (converted from Brinell hardness) | 71 | 71 |
| Hardness, Vickers (converted from Brinell hardness) | 131 | 131 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 70 | 70 |
Scope of Application
AISI 1018 carbon steel is commonly used in high volume screw machine parts applications. The other applications of this alloy are as follows:
● Shafts
● Spindles
● Pins
● Rods
● Sprocket assemblies.
What is your working time?
In general, our online service time is Beijing time: 8:00-22:00, after 22:00, we will reply to your inquiry during the next working day.
How to pack the products?
The inner layer has a waterproof paper outer layer with iron packaging and is fixed with a fumigation wooden pallet. It can effectively protect products from corrosion during ocean transportation.
Can you send samples?
Of course, we can send samples to all parts of the world, our samples are free, but customers need to bear the courier costs.
What product information do I need to provide?
You need to provide the grade, width, thickness, coating and the number of tons you need to purchase.
What are the shipping ports?
Under normal circumstances, we ship from Shanghai, Tianjin, Qingdao, Ningbo ports, you can choose other ports according to your needs.
About product prices?
Prices vary from period to period due to cyclical changes in the price of raw materials.
What are the certifications for your products?
We have ISO 9001, SGS, EWC and other certifications.
How long does your delivery time take?
In general, our delivery time is within 30-45 days, and may be delayed if the demand is extremely large or special circumstances occur.