Carbon Steel Coil
Carbon Steel Coil
1008 Cold Rolled Steel Coil
1008 carbon steel coil is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms. 1008 in the cold rolled condition is used for exposed or unexposed parts where bending, moderate drawing, forming and welding may be involved.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
1008 Cold Rolled Steel Coil
1008 cold rolled steel coil contains about 1.2% manganese and 0.4% silicon. There are also nickel, aluminium, chromium, copper and molybdenum present in small quantities in the carbon steels. AISI 1008 carbon steel coil has excellent weldability, which includes projection, butt, spot and fusion, and brazeability. 1008 cold rolled steel coil is mainly used in automobile, printed metal pail, building, building materials, and bicycle, etc. Besides, it is the best material to manufacture organic coated strip.
Product Parameters
Product Name | 1008 Cold Rolled Steel Coil |
Production Process | Hot Rolling, Cold Rolling |
Material Standards | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc. |
Width | 100mm-3000mm |
Length | 1m-12m, or Customized Size |
Thickness | 0.1mm-400mm |
Delivery Conditions | Rolling, Annealing, Quenching, Tempered or Standard |
Surface Process | Ordinary, Wire Drawing, Laminated Film |
Chemical Composition
| Element | Content (%) |
|---|---|
| Iron, Fe | 99.31-99.7 % |
| Manganese, Mn | 0.30-0.50 % |
| Carbon, C | 0.10 % |
| Sulfur, S | 0.050 % |
| Phosphorous, P | 0.040 % |
Mechanical Properties
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 340 MPa | 49300 psi |
| Yield strength (depending on temper) | 285 MPa | 41300 psi |
| Elastic modulus | 190-210 Gpa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 200 GPa | 29000 ksi |
| Shear modulus (typical for steel) | 80.0 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 20 % | 20 % |
| Reduction of area | 45 % | 45 % |
| Hardness, Brinell | 95 | 95 |
| Hardness, Knoop (converted from Brinell hardness) | 113 | 113 |
| Hardness, Rockwell B (converted from Brinell hardness) | 55 | 55 |
| Hardness, Vickers (converted from Brinell hardness) | 98 | 98 |
Machinability (based on AISI 1212 steel as 100 machinability) The machinability of group I bar, rod, and wire products can be improved by cold drawing) | 55 | 55 |
Scope of Application
AISI 1008 carbon steel is primarily used in extruded, cold headed, cold upset, and cold pressed parts and forms.
What is your working time?
In general, our online service time is Beijing time: 8:00-22:00, after 22:00, we will reply to your inquiry during the next working day.
How to pack the products?
The inner layer has a waterproof paper outer layer with iron packaging and is fixed with a fumigation wooden pallet. It can effectively protect products from corrosion during ocean transportation.
Can you send samples?
Of course, we can send samples to all parts of the world, our samples are free, but customers need to bear the courier costs.
What product information do I need to provide?
You need to provide the grade, width, thickness, coating and the number of tons you need to purchase.
What are the shipping ports?
Under normal circumstances, we ship from Shanghai, Tianjin, Qingdao, Ningbo ports, you can choose other ports according to your needs.
About product prices?
Prices vary from period to period due to cyclical changes in the price of raw materials.
What are the certifications for your products?
We have ISO 9001, SGS, EWC and other certifications.
How long does your delivery time take?
In general, our delivery time is within 30-45 days, and may be delayed if the demand is extremely large or special circumstances occur.