Hastelloy B3 bar has better strength and corrosion resistance at high temperatures compared with traditional Hastelloy. B3 alloy shows excellent stability and durability, especially in oxidizing and reducing environments, as well as corrosive environments such as strong acid and strong alkali.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
Hastelloy B-3 Bar Description
Hastelloy B3 is a nickel-based high-temperature alloy, mainly composed of nickel, molybdenum, cobalt and other elements. This alloy material is optimized on the basis of Hastelloy B2. Improving the thermal stability of the material significantly enhances the corrosion resistance, while also effectively improving the hot forming and cold forming performance. Hastelloy B3 bars have been increasingly used in the production and manufacturing of chemical equipment. Besides, Hastelloy B3 material has many unique properties. Its high elongation provides favorable conditions for cold forming operations. Compared to austenitic stainless steel, Hastelloy B3 bar is harder and therefore requires greater pressure during cold forming or step forming processes.
Product Parameters
Product Name | Hastelloy B-3 Bar | |
Outer Diameter | Round Bar | 4mm-500mm |
Hexagon Bar | 18mm-57mm (11/16″ to 2-3/4″) | |
Square Bar | 18mm-47mm (11/16″ to 1-3/4″) | |
Flat Steel | 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized | |
Length | 1-6 meters, Length can be customized | |
Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, NO.4, BA, etc. | |
Certificate | ISO, SGS, BV | |
Production Technology | Hot Rolling, Cold Rolling | |
Chemical Composition
C | Al | Si | P | S | Ti | V | Cr | Mn | Fe | Co | Ni | Cu | Zr | Nb | Mo | Ta | W | Not MO |
0.01 max | 0.5 max | 0.10 max | 0.03 max | 0.01 max | 0.2 max | 0.2 max | 1.0 - 3.0 | 3.0 max | 1.0 - 3.0 | 3.0 max | 65.0 min | 0.2 max | 0.1 max | 0.2 max | 27.0 - 32.0 | 0.2 max | 3.0 max | 94.0 - 98.0 |
Mechanical Properties
Tensile Strength (ksi) | 0.2% Yield Strength (ksi) | Elongation% in 2 inches |
110 | 51 | 40 |
Physical Performance
Units | Temperature in°C | |
Density | 9.22 g/cm³ | Room |
Specific Heat | 0.089 Kcal/kg.C | Room |
Melting Range | 1370-1418°C | - |
Modulus of Elasticity | 216 KN/mm² | Room |
Electrical Resistivity | 137 µΩ.cm | Room |
Coefficient of Expansion | 10.6 µm/m °C | 25 - 100° |
Thermal Conductivity | 11.2 w/m-° K | Room |
Scope of Application
B- 3 is used in chemical processes, vacuum furnaces, mechanical parts in reduced pressure environments, etc.