Stainless Steel Plate
Stainless Steel Plate
305 Stainless Steel Plate
305 stainless steel is a common austenitic stainless steel containing elements such as chromium, nickel, and manganese. Chromium is the main anti-corrosion element and can combine with oxygen to form a dense oxide film to protect materials from corrosion. Nickel can improve the material's heat resistance and toughness while reducing its magnetism. Manganese can increase the strength and hardness of materials.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
305 Stainless Steel Plate Description
305 stainless steel is an austenitic chromium-nickel stainless steel with a low work hardening rate. This low work hardening rate makes it suitable for many deep drawing applications. In order to minimize the earrings during the drawing process, the directionality introduced during the cold rolling process must be kept to a minimum.
Product Parameters
Product Name 305 Stainless Steel Plate Type Plate Thickness 0.3mm-200mm Length 2000mm, 2438mm, 3000mm, 5800mm, 6000mm, 12000mm, etc. Width 40mm-600mm, 1000mm, 1219mm, 1500mm, 1800mm, 2000mm, 2500mm, 3000mm, 3500mm, etc. Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface BA, 2B, NO.1, NO.4, 4K, HL, 8K, etc. Scope of Application Widely used in high temperature and electrical industry, medical equipment construction, chemical, food industry, agriculture and ship parts, food and beverage packaging, Kitchen supplies, trains, airplanes, conveyor belts, vehicles, bolts, nuts, springs and screens, etc. Certificate ISO, SGS, BV, etc. Production Technology Hot Rolling, Cold Rolling Edge Processing Edging, Trimming
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.04 ≤ 0.75 ≤ 2.0 17.0～19.0 10.5～13.0 ≤ 0.03 ≤ 0.045
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥515 ≥205 ≥35 ≤ 187HB;≤ 90HRB;≤ 200HV
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(ΜΩ. cm) 7.99 193 17.3 16.2 72
Surface Selection