Stainless Steel Bar
Stainless Steel Bar
405 Stainless Steel Bar
405 stainless steel is categorized as austenitic stainless steel material that is resistant to corrosion with good mechanical properties. The bars are usually used as manufacturing parts in marine engineering, petrochemical industry, food processing and other fields.
Big fire special steel, high strength steel plate, steel industry supply and demand, steel suppliers
405 Stainless Steel Bar Description
The mechanical properties of 405 stainless steels are important in determining their suitability for various applications. This steel has excellent workability and is easy to cut and shape into different shapes. In addition, the material exhibits a good level of strength and hardness, making it wear-resistant and tear-resistant. A remarkable characteristic of 405 stainless steel is its ductility, which refers to its ability to deform under pressure without breaking. This property makes the metal suitable for forming processes such as bending and rolling without cracking or breaking.
Product Parameters
Product Name 405 Stainless Steel Bar Type Steel Bar Outer Diameter Round Bar 4mm-500mm Hexagon Bar 18mm-57mm (11/16″ to 2-3/4″) Square Bar 18mm-47mm (11/16″ to 1-3/4″) Flat Steel 1/2 "to 10", Thickness: 2mm-150mm, Can provide customized Length 1-6 meters, Length can be customized Standard ASTM, AISI, JIS, GB, DIN, EN, etc. Surface Black, Bright Polished, Rough Turning, Mattness Surface Treatment, No. 4. BA, etc. Scope of Application Stainless steel bars are used in a variety of industries such as shipbuilding, Defense, Automotive, Textiles, Paper and pulp, Manufacturing, Cement, Heavy earthmoving equipment and construction, etc.
Chemical Composition
C Si Mn Cr Ni S P ≤ 0.08 ≤1.0 ≤1.0 11.5～14.5 ≤ 0.5 ≤ 0.03 ≤ 0.04
Mechanical Properties
Tensile Strength Kb (MPa) Yield Strength σ0.2 (MPa) Elongation D5 (%) Hardness ≥485 ≥275 ≥25 ≤ 160HBW
Physical Performance
Density(g/cm³) Modulus of Elasticity(Gpa) Coefficient of Thermal Expansion(10-6/°C) Coefficient of Thermal Conductivity(W/m*K) Resistivity(Ω.mm2/m) 7.80 200 10.8 27.0 0.6